Effective copolymerization of ethylene with α,ω-alkenols and homopolymerization of α,ω-alkenols catalyzed by aminophenolate zirconium complex
2019
Abstract A zirconium complex of diamine-bis(phenolate) ligand, [(tBu2O2NN’)ZrCl]2(μ-O) where (tBu2O2NN’) = Me2N(CH2)2N(CH2–2-O−-3,5-tBu2-C6H2)2, activated with (iBu)3Al/Ph3CB(C6F5)4, was for the first time used in copolymerization of ethylene with unsaturated alcohols (CH2 = CH(CH2)nCH2OH, where n = 7, 8, 3). The hydroxyl groups of comonomers were protected with R3-xAlClx (where x = 0 or 1, R = iBu, Et). In contrast to the formerly reported catalysts, the activity of this catalyst is much higher in ethylene/alkenols copolymerization than in ethylene homopolymerization and its lifetime is long. Moreover, the copolymers with high polar comonomer contents (up to 16.4 mol%, 52.3 wt%) were produ…
POSS Grafting on Polyethylene and Maleic Anhydride-Grafted Polyethylene by One-Step Reactive Melt Mixing
2018
This study reports the one-step reactive melt mixing preparation of organic-inorganic hybrid based on maleic anhydride-grafted polyethylene and 3-(2-aminoethyl)aminopropyl-heptaisobutyl substituted polyhedral oligomeric silsesquioxane, (NPOSS), as well as on low-density polyethylene and allyl-heptaisobutyl-POSS (1POSS) in dicumyl peroxide presence, which is believed to activate the unsaturation of the reactive functional group of POSS itself. The successful grafting of POSS molecules onto polymeric backbones was probed through rheological and spectroscopic analysis. Grafting of POSS molecules enhances their dispersion in the polymeric matrix as shown by morphological analysis. Moreover, the…
Effect of interfacial area on heterogeneous free radical grafting of vinyl monomers in supercritical carbon dioxide: Grafting of acrylic acid on poly…
2014
The role of the polymer interfacial area on free radical grafting of acrylic acid (AA) onto poly(vinylidenefluoride) (PVDF) was studied at 65°C using supercritical carbon dioxide (scCO2) as a solvent and swelling agent, benzoylperoxide (BPO) as chemical initiator and PVDF nanoparticles as polymer matrix. Under adopted conditions PVDF particles do not melt neither dissolve in the reaction medium and FTIR analyses performed on carefully washed nanoparticles confirmed the achievement of high grafting levels. The mass fraction of grafted AA increased with the grafting time and the BPO concentration while it decreased when the density of the fluid phase was enhanced. Collected results suggest th…